It has been observed that the flow stress of a nickel single crystal can be lowered about 15% by applying an alternating magnetic field parallel to the specimen axis during plastic deformation at -194°C. This phenomenon, named by us as the magneto-plastic effect, can be interpreted qualitatively in terms of a concept that oscillating magnetic domain walls give a force on dislocations. In order to clarify this effect, its dependence on the temperature, plastic strain, strain rate, and on the strength and frequency of the alternating magnetic field applied have been measured. The activation volumes in relation to a thermally activated process of dislocation motion were also obtained from the stress relaxation curves measured after and before the application an alternating magnetic field, and they were compared mutually at various values of the shear stress.
References
- 1 W. F.Brown: Phys. Rev. 58 (1940) 736. Crossref, Google Scholar
- 2 W. F.Brown: Phys. Rev. 60 (1941) 139. Crossref, Google Scholar
- 3 R. M.Bozorth: Ferromagnedsm (D. van Nostrand Co., 1951) p. 595. Google Scholar
- 4 M.Kersten: Z. angew. Phys. 8 (1956) 313, 382 and 496. Google Scholar
- 5 H.Kronmüller: Z. Phys. 154 (1959) 574. Crossref, Google Scholar
- 6 H.Kronmüller and A.Seeger: J. Phys. Chem. Solids 18 (1961) 93. Crossref, Google Scholar
- 7 F.Vicena: Czech. J. Phys. 5 (1955) 480. Crossref, Google Scholar
- 8 T.Huzimura: Trans. Japan Inst. Metals 2 (1961) 182. Crossref, Google Scholar
- 9 H.Träuble: Moderne Probleme der Metallphysik ed. A.Seeger (Springer-Verlag, Berlin, 1966) Vol. 2, p. 157. Crossref, Google Scholar
- 10 H.Träuble and A.Seeger: Z. angew. Phys. 21 (1966) 299. Google Scholar
- 11 D.Krause: Z. Phys. 168 (1962) 239. Crossref, Google Scholar
- 12 A.Seeger, H.Kronmüller, H.Rieger and H.Träuble: J. appl. Phys. 35 (1964) 740. Crossref, Google Scholar
- 13 H.Bilger: Phys. Status solidi 18 (1966) 207. Crossref, Google Scholar
- 14 S.Hayashi: Trans. Japan Inst. Metals 8 (1967) 207. Crossref, Google Scholar
- 15 A. H.Cottrell: Dislocation and Plastic Flow (Oxford University, Oxford, 1953) p. 32. Google Scholar
- 16 S.Hayashi, S.Takahashi and M.Yamamoto: J. Phys. Soc. Japan 25 (1968) 910. Link, Google Scholar
- 17 H.Kronmüller: Moderne Probleme der Metallphysik ed A.Seeger (Springer-Verlag, Berlin, 1966) Vol. 2, p. 81. Google Scholar
- 18 M.Peach and J. S.Koehler: Phys. Rev. 80 (1950) 436. Crossref, Google Scholar
- 19 P.Haasen: Phil. Mag. 3 (1958) 384. Crossref, Google Scholar
- 20 A.Seeger: Dislocations and Mechanical Properties of Crystals ed. J. C.Fisher (Wiley, New York, 1957) p. 243. Google Scholar